Si,% | S,% | 温度,℃ | 带渣量,% |
≤0.60 | ≤0.050 | ≥1250 | ≤0.8 |
P,% | Mn,% | Cr,% | Ni,% | Cu,% |
≤0.150 | ≤0.70 | ≤0.10 | ≤0.10 | ≤0.04 |
Si,% | S,% | P,% | Mn,% | Cr,% | As,% | Cu,% | 温度,℃ |
≤0.8 | ≤0.07 | ≤0.15 | ≤0.7 | ≤0.1 | ≤0.03 | ≤0.02 | ≥1250 |
TFe,% | Si,% | S,% | P,% |
≥92 | ≤1.50 | ≤0.070 | ≤0.30 |
Mn,% | SiO2,% | S,% | P,% | 粒度,mm |
≥28 | ≤18 | ≤0.030 | ≤0.40 | 20~150,且20~150比例应≥90% |
TFe,% | SiO2,% | S,% | H2O,% |
≥52 | ≤3.0 | ≤0.12 | ≤4.0 |
粒度:7mm-60mm,<7mm比例≤10% | |||
牌号 | Mn,% | Si,% | C,% | P,% | S,% | ||
Ⅰ | Ⅱ | Ⅲ | |||||
不大于 | |||||||
FeMn68Si18 | ≥65 | ≥17 | 1.8 | 0.10 | 0.15 | 0.25 | 0.04 |
FeMn68Si16 | ≥65 | ≥17 | 2.5 | 0.10 | 0.15 | 0.25 | 0.04 |
粒度10~100mm,粒度<10mm比例≤5%,粒度>100mm比例≤5% | |||||||
类别 | 牌号 | C,% | Si,% | Mn,% | P,% | S,% | ||
Ⅰ | Ⅱ | Ⅰ | Ⅱ | |||||
低碳 锰铁 | FeMn84C0.7 | ≤0.7 | ≤1.0 | ≤2.0 | 80~87 | ≤0.20 | ≤0.30 | ≤0.020 |
中碳 锰铁 | FeMn82C1.5 | ≤1.5 | ≤1.5 | ≤2.0 | 78~85 | ≤0.20 | ≤0.35 | ≤0.030 |
农行核心价值观 FeMn82C2.0 | ≤2.0 | ≤1.5 | ≤2.5 | 75~82 | ≤0.20 | ≤0.40 | ≤0.030 | |
高碳 锰铁 | FeMn68 | ≤7.0 | ≤1.0 | ≤2.0 | 65~70 | ≤0.30 | ≤0.40 | ≤0.030 |
FeMn68C7.0 | ≤7.0 | ≤2.5 | ≤4.5 | 65~72 | ≤0.25 | ≤0.40 | ≤0.030 | |
粒度10~100mm,粒度<10mm比例≤5%,粒度>100mm比例≤5% | ||||||||
牌号 | Si,% | 自然块粒度, mm | 合格块粒度, mm |
FeSi75-C | 74~80 | <20×20mm比例≤8% | 20~80mm,<20×20mm比例≤8%, 80-100mm比例≤5% |
FeSi75Al0.5-B | 72~80 | ||
牌号 | Si,% | Al,% | Mn,% | C,% | P,% | S,% |
不小于 | 不大于 | |||||
FeAl42Si15 | 15 | 42 | 0.2 | 0.2 | 0.02 | 0.02 |
FeAl35Si25 | 25 | 35 | 0.2 | 0.2 | 0.015 | 0.02 |
粒度10~150mm,粒度<10mm比例≤5%,>150mm比例≤5%,单重10kg/袋 | ||||||
Si,% | 粒度 |
≥12 | 粒度10~150mm,粒度<10mm比例≤5% |
牌号 | Si,% | Ca,% | Ba,% | Al,% |
不小于 | ||||
Al8Ba12Ca6Si40 | 40.0 | 6.0 | 12.0 | 8.0 |
粒度10~100mm,粒度<10mm比例≤5%,粒度>100mm比例≤5%;单重20 kg/袋(内装5Kg小袋) | ||||
Al,% | Si,% | S,% | P,% | Fe,% | 单重,Kg/袋 |
48~52 | ≤1.0 | ≤0.040 | ≤0.040 | 余量 | 10±0.05 |
粒度10~100mm,粒度<10mm比例≤5%,粒度>100mm比例≤5% | |||||
牌号\化学成分 | Ca,% | Si % | C,% | Al,% | P,% | S,% |
不小于 | 不大于 | |||||
Ca24Si60 | 24.0 | 55~65 | 1.0 | 2.5 | 0.04 | 0.04 |
最大块重≤10kg,<15mm×15mm比例<10% | ||||||
C,% | Si,% | Mn,% | Al,% | P,% | S,% | 单重,Kg/袋 |
≤1.5 | ≤1.0 | ≥30 | ≥20 | ≤0.25 | ≤0.05 | 10±0.05 |
粒度要求:10~100mm,<10mm比例≤5%,>100mm比例≤5% | ||||||
牌号 | V,% | 中华慈善总会会长 C,% | Si,% | P,% | S,% | Al,% | Mn,% |
不大于 | |||||||
FeV50A | 48-55 | 0.4 | 2.0 | 0.06 | 0.04 | 1.5 | |
FeV50B | 48-55 | 0.6 | 3.0 | 0.10 | 0.06 | 2.5 | |
FeV50C | 48-55 | 5.0 | 3.0 | 0.10 | 0.06 | 0.5 | |
FeV60A | 58-65 | 0.4 | 2.0 | 0.06 | 0.04 | 1.5 | |
FeV60B | 58-65 | 0.6 | 2.5 | 0.10 | 0.06 | 2.5 | |
FeV60C | 58-65 | 3.0 | 1.5 | 0.10 | 0.06 | 0.5 | |
FeV80A | 78-82 | 0.15 | 1.5 | 0.05 | 0.04 | 1.5 | 0.50 |
FeV80B | 78-82 | 0.30 | 1.5 | 0.08 | 0.06 | 2.0 | 0.50 |
FeV80C | 75-80 | 0.30 | 1.5 | 0.08 | 0.06 | 2.0 | 0.50 |
粒度范围10~50mm,粒度<10mm比例≤5%,粒度>50mm比例≤5% | |||||||
牌号 | Ti,% | Al,% | Si,% | P,% | S,% | C,% | Cu,% | Mn,% |
不大于 | ||||||||
FeTi30-A | 25~35 | 8.0 | 4.5 | 0.05 | 0.03 | 0.10 | 0.10 | 2.5 |
FeTi30-B | 25~35 | 8.5 | 5.0 | 0.07 | 0.04 | 有那样一个下午0.20 | 0.20 | 2.5 |
FeTi40-A | >35~45 | 9.0 | 3.5 | 0.05 | 0.03 | 0.10 | 0.20 | 2.5 |
FeTi40-B | >35~45 | 9.5 | 4.0 | 0.08 | 0.04 | 0.20 | 0.40 | 3.0 |
FeTi50-B | >45~55 | 9.5 | 4.0 | 0.08 | 0.04 | 0.20 | 0.40 | 3.0 |
FeTi60-A | >55~65 | 7.0 | 3.0 | 0.04 | 0.03 | 0.10 | 0.20 | 1.0 |
FeTi60-B | >55~65 | 8.0 | 4.0 | 0.06 | 0.04 | 0.20 | 0.20 | 1.5 |
FeTi60-C | >55~65 | 8.5 | 5.0 | 0.08 | 0.04 | 0.30 | 0.20 | 2.0 |
FeTi70-A | >65~75 | 3.0 | 0.5 | 0.04 | 0.03 | 0.10 | 0.20 | 1.0 | 杂交鹅
FeTi70-B | >65~75 | 6.0 | 3.5 | 0.06 | 0.04 | 0.20 | 0.20 | 1.0 |
FeTi70-C | >65~75 | 8.0 | 4.0 | 0.08 | 0.04 | 0.40 | 0.20 | 1.0 |
FeTi80-A | >75 | 3.0 | 0.5 | 0.04 | 0.03 | 0.10 | 0.20 | 1.0 |
FeTi80-B | >75 | 6.0 | 3.5 | 0.06 | 0.04 | 0.20 | 0.20 | 1.0 |
FeTi80-C | >75 | 7.0 | 4.0 | 0.08 | 0.04 | 0.40 | 0.20 | 1.0 |
粒度范围10~50mm,粒度<10mm比例≤5%,粒度>50mm比例≤5% | ||||||||
类别 | 牌号 | Cr,% | C,% | Si,% | P,% | S,% |
不大于 | ||||||
微碳 | FeCr55C6 | ≥60 | 0.06 | 2.0 | 0.06 | 0.03 |
低碳 | FeCr55C25 | ≥60 | VBR0.25 | 3.0 | 0.06 | 0.05 |
中碳 | FeCr55C100 | ≥60 | 1.0 | 3.0 | 0.06 | 0.05 |
中碳 | FeCr55C200 | ≥60 | 2.0 | 3.0 | 0.06 | 0.05 |
高碳 | FeCr55C600 | ≥60 | 6.0 | 5.0 | 0.06 | 0.06 |
粒度要求:10~50mm,粒度<10mm 的比例≤5 % | ||||||