硅烷交联高密度聚乙烯热收缩材料性能的研究

10.16638/jki.1671-7988.2020.05.061

林博，李智

（华晨汽车工程研究院车身部，辽宁沈阳110142）

摘要：利用硅烷交联的工艺方法制备了高密度聚乙烯（HDPE）热收缩材料，研究了引发剂过氧化二异丙苯（DCP）和过氧化二特丁烷（DTBP）含量的变化对复合热收缩材料拉伸强度、断裂伸长率、维卡软化点、凝胶含量和热收缩率的影响。结果表明：通过试验确认了当引发剂加入0.12份时，制备出来的复合热收缩材料综合性能最好。相比之下，DTBP作为引发剂对复合体系性能影响效果更显著。

关键词：高密度聚乙烯；硅烷交联；引发剂；凝胶含量

中图分类号：TQ325.1 文献标识码：A 文章编号：1671-7988(2020)05-219-03

Research on Thermal Shrinkable Materials of Silane Cross-linked HDPE凤凰2009

仿生学论文

Lin Bo, Li Zhi

（Brilliance Automotive Engineering Research Institute, Liaoning Shenyang 110142）

Abstract: The HDPE thermal shrinkable materials were prepared by silane crosslinking. The effects of the contents of DCP and DTBP on the tensile strength, elongation at break, softening point, gel content and thermal shrinkage of the composite thermal shrinkable materials were studied. The results showed that the composite heat shrinkable material had the best comprehensive performance when 0.12 initiator was added. In contrast, the effect of DTBP as initiator on composite system performance is more significant.

Keywords: HDPE; Silane cross-linking; Initiator; Gel content

CLC NO.: TQ325.1 Document Code: A Article ID: 1671-7988(2020)05-219-03

前言

热收缩材料又称高分子形状记忆材料，是高分子材料与辐射加工技术结合的一种智能型材料，即利用高分子聚合物“弹性记忆”原理，以橡塑材料为基料，经混炼、成型、交联、加热、扩张、冷却定型而制成的功能性高分子材料[1]。

咱们的退伍兵

热收缩材料都具有两相结构，即由记忆起始形状的固定相和随温度变化而可逆地固化、软化的可逆相组成[2]。共聚物交联反应后，大分子的加入使分子间链段伸展、运动，撤去外力可恢复原状，此种现象称之为高弹形变。经交联反应，原来的线形结构转变成三维立体网状结构，加热到其熔点以上时不再熔化，而且在很宽的温度范围内表现出弹性体的性质。

聚乙烯(PE)的交联技术是聚乙烯改性的重要手段之一[3]。交联聚乙烯与普通聚乙烯相比，具有卓越的电绝缘性能和更高的冲击强度及拉伸强度，具有突出的耐磨性，优良的耐应力开裂性、耐蠕变性及尺寸稳定性，耐热性、耐低温性、耐老化性、耐化学药品性、耐辐射性也很好。因而被广泛应用于化工、建筑、汽车、机械、电力、包装、农业等行业。近年来，国内外在聚乙烯交联改性方面的研究开发非常活跃[4]。

新语丝网站1 实验部分

1.1 主要原料

radarsat高密度聚乙烯(HDPE，齐鲁石化)；乙烯基三乙氧基硅烷

作者简介：林博，工程师，研究生，就职于华晨汽车工程研究院，

研究方向为汽车非金属材料改性。