牌号 | Br | Hcb | (BH)m | |
Y20 | 3700 ± 100GS | 2.9±0.3Mgoe | Ba | |
370 ± 10MT | 135.5~160KA/m2 | 23.1KJ/m3 | ||
Y25 | 3800 ± 100GS | 2010 ~2380oe | 3.2±0.3Mgoe | Ba |
380 ± 10MT | 160~189.7KA/m2性别大战 | 25.5KJ/m3 | ||
Y30 | 3900 ± 100GS | 2220 ± 200oe | 3.5±0.2Mgoe | SI |
390 ± 10MT | 177 ± 16KA/m2 | 30.3~33.4KJ/m3 | ||
Y35 | 4000 ± 100GS | 2400~2600oe | 4.0±0.2Mgoe | SI |
400 ± 10MT | 191.3~207.2A/m2 | 30.3KJ/m3 | ||
材料 牌号 Type | 剩余磁感应强度 Residual Induction | 磁感矫顽力 Coeyciive Force | 内禀矫顽力 Intrinsic Coercivity | 最大磁能积Maximum Energy Product | 最高工作 温度Max. Operation Temp. | 回复 磁导 率 | |||
Br | bHC | jHc | (BH)max | r | |||||
kGs | T | KOe | KA/m | KOe | MGOe | KJ/m3 | ℃ | ||
N42 | 13~13.4 | 1.3~1.34 | 11.0~12.0 | 876~955.2 | ≥12 | 41~43 | 326~342 | 80 | 1.05 |
N40 | 12.8~13.2 | 1.28~1.32 | 11.0~13.0 | 876~1035 | ≥12 | 39~41 | 310~326 | 80 | 1.05 |
N38 | 12.4~12.7 | 1.24~1.27 | 12.0~14.0 | 955~1114 | ≥12 | 37~39 | 295~310 | 80 | 1.05 |
N35 | 11.9~12.2 | 1.19~1.22 | 12.0~14.0 | 955~1114 | ≥17 | 34~36 | 271~287 | 80 | 1.05 |
N38H | 12.4~12.7 | 1.24~1.27 | >17.0 | 夏普sh8298u>1353 | ≥17 | 37~39 | 295~310 | 120 | 1.05 |
N35H | 11.9~12.2 | 1.19~1.22 | >17.0 | >1353 | ≥船用接触器17 | 34~36 | 271~287 | 120 | 1.05 |
N33H | 11.5~11.7 | 1.15~1.17 | >17.0 | >1353 | ≥17 | 32~34 | 254~270 | 120 | CDN 服务器1.05 |
N30H | 10.8~11.2 | 1.08~1.12 | >17.0 | >1353 | ≥17 | 29~31 | 231~247 | 120 | 1.05 |
N33SH | 11.3~11.7 | 1.13~1.17 | >21.0 | >1672 | ≥17 | 31~33 | 247~263 | 120 | 1.05 |
N30UH | 10.8~11.2 | 1.08~1.12 | >25.0 | >1990 | ≥17 | 29~31 | 231~247 | 120 | 1.05 |
N26UH | 10.5~10.9 | 1.05~1.09 | >25.0 | >1990 | ≥17 | 26~28 | 207~223 | 120 | 1.05 |
约束机制N38SH | 12.9~13.3 | 1.29~1.33 | >21.0 | >1672 | ≥21 | 40~36 | 318~287 | 150 | - |
密度Density 均为7.5 g/cm3 | |||||||||