序号 | 统一数字 代号 | 牌号 | 化学成分(质量分数)(%) | |||||
C | Si | Mn | Cr | M | Cu | |||
≤ | ||||||||
1 | U20080 | 08F | O.05~O.11 | ≤0.03 | 0.25~0.50 | 0.10 | O.30 | 0.25 |
2 | U20l00 | 10F | O.07~O.13 | ≤O.07 | O.25~O.50 | O.15 | 0.30 | 0.25 |
3 | U20150 | 15F | 0.12~O.18 | ≤O.07 | 0.25~O.50 | 0.25 | 0.30 | 0.25 |
4 | U20082 | 08 | 0.05~O.11 | O.17~O.37 | O.35~O.65 | O.10 | O.30 | O.25 |
5 | U20102 | lO | 0.07~O.13 | 0.17~O.37 | 0.35~0.65 | 0.15 | O.30 | O.25 |
6 | U20152 | 15 | O.12~0.18 | 0.17~O.37 | O.35~0.65 | O.25 | O.30 | O.25 |
7 | U20202 | 20 | O.17~0.23 | 0.17~0.37 | 0.35~0.65 | O.25 | O.30 | O.25 |
8 | U20252 | 25 | O.22~0.29 | 0.17~O.37 | O.50~O.80 | O.25 | O.30 | 0.25 |
9 | U20302 | 30 | O.27~O.34 | O.17~O.37 | O.50~O.80 | 0.25 | O.30 | 0.25 |
10 | U20352 | 35 | O.32~0.39 | O.17~O.37 | O.50~O.B0 | 0.25 | O.30 | 0.25 |
11 | U20402 | 40 | 0.37~O.44 | 0.17~O.37 | O.50~O.80 | O.25 | O.30 | O.25 |
12 | U20452 | 45 | O.42_O.50 | O.17~O.37 | 0.50~0.80 | 0.25 | O.30 | 0.25 |
13 | U20502 | 50 | 0.47~0.55 | 0.17~O.37 | 0.50~0.80 | 0.25 | O.30 | O.25 |
14 | U20552 | 55 | O.52~0.60 | O.17~O.37 | O.50~0.80 | O.25 | 0.30 | O.25 |
15 | U20602 | 60 | 0.57~O.65 | 0.17~O.37 | 0.50~O.80 | O.25 | O.30 | 0.25 |
16 | U20652 | 65 | O.62~0.70 | 0.17~0.37 | O.50~O.80 | O.25 | O.30 | O.25 |
17 | U20702 | 70 | O.67~0.75 | 0.17~0.37 | O.50~O.80 | 0.25 | O.30 | O.25 |
18 | U20752 | 75 | O.72~0.80 | 0.17~O.37 | 0.50~0.80 | 0.25 | O.30 | O.25 |
19 | U20802 | 80 | O.77~0.85 | O.17~0.37 | O.50~O.80 | 0.25 | O.30 | 0.25 |
20 | U20852 | 85 | O.82~0.90 | O.17~0.37 | 0.50~O.80 | O.25 | O.30 | O.25 |
21 | U21152 | 15№ | O.12~O.18 | O.17~O.37 | O.70~1.00 | O.25 | O.30 | 0.25 |
22 | U21202 | 20Mn | 0.17~O.23 | O.17~O.37 | O.70~1.00 | O.25 | 0.30 | O.25 |
23 | U21252 | 25Mn | O.22~O.29 | 0.17~0.37 | O.70~1.00 | O.25 | O.30 | O.25 |
24 | U21302 | 30Mn | 0.27~O.34 | O.17~0.37 | 0.70~1.00 | O.25 | O.30 | 0.25 |
25 | U21352 | 1973号决议 35Mn | O.32~O.39 | O.17~O.37 | O.70~1.00 | 0.25 | O.30 | O.25 |
26 | U21402 | 40Mn | O.37~0.44 | O.17~0.37 | O.70~1.00 | 0.25 | 0.30 | O.25 |
27 | U21452 | 45Mn | 0.42~0.50 | 0.17~O.37 | 0.70~1.00 | O.25 | O.30 | O.25 |
28 | U21502 | 50Mn | 邻苯二甲酸酐O.48~0.56 | O.17~O.37 | O.70~1.00 | 0.25 | 0.30 | 0.25 |
29 | U21602 | 60Mn | 0.57~0.65 | O.17~O.37 | 0.70~1.00 | 0.25 | 0.30 | 0.25 |
30 | U21652 | 65Mn | 0.62~0.70 | 0.17~O.37 | O.90~1.20 | O.25 | 0.30 | 0.25 |
3l | U21702 | 70Mn | 0.67~O.75 | 0.17~0.37 | 0.90~1.20 | O.25 | O.30 | O.25 |
组 别 | P | S |
(%)≤ | ||
优质钢 | 0.035 | 0.035 |
高级优质钢 | 0.030 | 0.030 |
特级优质钢 | 0.025 | O.020 |
牌号 | 试样毛坯尺寸/mm | 推荐热处理/℃ | 力学性能 | 钢材交货状态硬度HBSl0/300≤ | |||||||||||||||
正火 | 淬火 | 回火 | ób/MPa | ós/MPa | δ5(%) | Ψ(%) | AKu2/J | ||||||||||||
≥ | 未热处理钢 | 退火钢 | |||||||||||||||||
08F | 25 | 930 | 295 | 175 | 35 | 60 | 13l | ||||||||||||
10F | 25 | 930 | 315 | 185 | 33 | 55 | 137 | ||||||||||||
15F | 25 | 920 | 355 | 205 | 29 | 55 | 143 | ||||||||||||
08 | 25 | 930 | 325 | 195 | 33 | 60 | 131 | ||||||||||||
IO | 篮 | 930 | 335 | 读心术揭秘205 | 3l | 55 | 137 | ||||||||||||
15 | 25 | 920 | 375 | 225 | 27 | 55 | 143 | ||||||||||||
20 | 25 | 910 | 4lO | 245 | 25 | 55 | 156 | ||||||||||||
25 | 25 | 900 | 870 | 600 | 450 | 275 | 23 | 50 | 71 | 170 | |||||||||
30 | 25 | 880 | 860 | 600 | 490 | 295 | 21 | 50 | 63 | 179 | |||||||||
35 | 25 | 870 | 850 | 600 | 530 | 315 | 20 | 45 | 55 | 197 | |||||||||
40 | 25 | 860 | 840 | 60D | 570 | 335 | 19 | 45 | 47 | 217 | 187 | ||||||||
45 | 25 | 850 | 840 | 600 | 600 | 355 | 16 | 40 | 39 | 229 | 197 | ||||||||
50 | 25 | 830 | 830 | 600 | 630 | 375 | 14 | 40 | 31 | 24l | 207 | ||||||||
55 | 25 | 820 | 820 | 600 | 645 | 380 | 13 | 35 | 255 | 217 | |||||||||
60 | 25 | 810 | 675 | 400 | 12 | 35 | 255 | 229 | |||||||||||
65 | 25 | 810 | 695 | 410 | lO | 30 | 255 | 229 | |||||||||||
70 | 25 | 790 | 715 | 420 | 9 | 30 | 269 | 229 | |||||||||||
75 | 试样 | 820 | 480 | 1080 | 880 | 7 | 30 | 285 | 24l | ||||||||||
80 | 试样 | 820 | 480 | 1080 | 930 | 6 | 30 | 285 | 241 | ||||||||||
85网页没有地址栏 | 试样 | 820 | 480 | 1130 | 980 | 6 | 30 | 302 | 255 | ||||||||||
15Mn | 25 | 920 | 410 | 245 | 26 | 55 | 163 | ||||||||||||
20Mn | 25 | 910 | 450 | 275 | 24 | 50 | 197 | ||||||||||||
25Mn | 25 | 900 | 870 | 600 | 490 | 295 | 22 | 50 | 71 | 207 | |||||||||
30Mn | 25 | 880 | 860 | 600 | 540 | 315 | 20 | 45 | 63 | 217 | 187 | ||||||||
35Mn | 25 | 870 | 850 | 600 | 560 | 335 | 18 | 45 | 55 | 229 | 197 | ||||||||
40Mn | 25 | 860 | 840 | 600 | 590 | 平原往事小说355 | 17 | 45 | 47 | 229 | 207 | ||||||||
45Mn | 25 | 850 | 840 | 600 | 620 | 375 | 15 | 40 | 39 | 241 | 217 | ||||||||
50Mn | 25 | 830 | 830 | 600 | 645 | 390 | 13 | 40 | 3l | 255 | 217 | ||||||||
60Mn | 25 | 810 | 695 | 410 | 11 | 35 | 269 | 229 | |||||||||||
65Mn | 25 | 830 | 735 | 430 | 9 | 30 | 285 | 229 | |||||||||||
70Mn | 25 | 790 | 785 | 450 | 8 | 30 | 285 | 229 | |||||||||||
牌 号 | 主要特性 | 应用举例 |
08F | 优质沸腾钢,强度、硬度低,塑性极好。深冲压,深拉延性好,冷加工性,焊接性好 成分偏析倾向大,时效敏感性大,故冷加工时,可采用消除应力热处理,或水韧处理,防止冷加工断裂 | 易轧成薄板,薄带、冷变形材、冷拉钢丝 用作冲压件、压延件,各类不承受载荷的覆盖件、渗碳、渗氮、氰化件、制作各类套筒、靠模、支架 |
08 | 极软低碳钢,强度、硬度很低,塑性、韧性极好,冷加工性好,淬透性、淬硬性极差,时效敏感性比08F稍弱,不宜切削加工,退火后,导磁性能好 | 宜轧制成薄板、薄带、冷变形材、冷拉、冷冲压、焊接件、表面硬化件 |
1OF lO | 强度低(稍高于08钢),塑性、韧性很好,焊接性优良,无回火脆性。易冷热加工成型、淬透性很差,正火或冷加工后切削性能好 | 宜用冷轧、冷冲、冷镦、冷弯、热轧、热挤压、热镦等工艺成型,制造要求受力不大、韧性高的零件,如摩擦片、深冲器皿、汽车车身、弹体等 |
15F 15 | 强度、硬度、塑性与1OF、10钢相近。为改善其切削性能需进行正火或水韧处理适当提高硬度。淬透性、淬硬性低、韧性、焊接性好 | 制造受力不大,形状简单,但韧性要求较高或焊接性能较好的中、小结构件、螺钉、螺栓、拉杆、起重钩、焊接容器等 |
20 | 强度硬度稍高于15F,15钢,塑性焊接性都好,热轧或正火后韧性好 | 制作不太重要的中、小型渗碳、碳氮共渗件、锻压件,如杠杆轴、变速箱变速叉、齿轮,重型机械拉杆、钩环等 |