原料 | C | Si | Mn | P | S | 温度,℃ |
铁水 | 4.280 | 0.850 | 0.580 | 0.150 | 0.037 | 1250 |
废钢 | 0.18 | 0.20 | 0.52 | 0.022 | 0.025 | 25 |
名称 | CaO | 崇文门新世界店庆SiO2 | MgO | Al2O3 | S | P | CaF2 | FeO | Fe2O3 | 烧碱 | H2O | C |
石灰 | 91.0 | 2.0 | 2.0 | 1.5 | 0.05 | 3.45 | ||||||
矿石 | 1.0 | 5.61 | 0.52 | 1.10 | 0.07 | 29.4 | 61.8 | 0.50 | ||||
萤石 | 6.0 | 0.58 | 1.78 | 0.09 | 0.55 | 89.0 | 2.00 | |||||
生白云石 | 55.0 | 3.0 | 33.0 | 3.0 | 1.0 | 5.0 | ||||||
炉衬 | 54.0 | 2.0 | 38.0 | 1.0 | 5.0 | |||||||
项目 | 固态平均热容kJ/kg·K | 熔化潜热 kJ/kg | 液(气)态平均热容kJ/kg·K |
生铁 | 0.745 | 217.568 | 0.8368 |
钢 | 0.699 | 271.96 | 0.8368 |
炉渣 | 209.20 | 1.247 | |
炉气 | 1.136 | ||
烟尘 | 1.000 | 209.20 | |
矿石 | 1.046 | 209.20 | |
元素 | 反应 | 反应热,kJ/kg元素 |
C | [C]+1/2O2=CO | 10950 |
C | [C]+O2=CO2 | 34520 |
Si | [Si]+O2=SiO2 | 28314 |
P | 2[P]+5/2O2=P2O5 | 18923 |
Mn | [Mn]+1/2O2=MnO | 7020 |
Fe | [Fe]+1/2O2=FeO | 5020 |
Fe | [Fe]+3/2O2=Fe2O3 | 6670 |
SiO2 | SiO2+2CaO=2CaO·SiO2 | 2070 |
P2O5 | P2O5+4CaO=4CaO·P2O5 | 5020 |
元素,% 项目 | C | Si | 清教主义Mn | P | S |
铁水 | 4.28 | 0.85 | 0.58 | 0.150 | 0.037 |
钢水 | 0.18 | 0 | 0.17 | 0.015 | 0.025 |
氧化量 | 4.10 | 0.85 | 0.41 | 0.135 | 0.012 |
元素 | 反应 | 元素氧化量,kg | 耗氧量,kg | 氧化产物量,kg |
C | [C]+1/2O2=CO | 4.10×90%=3.69 | 3.69×16/12=4.82 | 3.69×28/12=8.61 |
C | [C]+O2=CO2 | 4.10×10%=0.41 | 0.41×32/12=1.503 | 0.41×44/12=1.503 |
Si | [Si]+O2=SiO2 | 0.85 | 0.85×32/28=0.972 | 0.85×60/28=1.82 |
Mn | [Mn]+1/2O2=MnO | 0.41 | 0.41×16/55=0.119 | 0.41×71/55=0.529 |
P | 2[P]+5/2O2=(P2O5) | 0.135 | 0.135×80/62=0.174 | 0.135×142/62=0.309 |
S | [S]+O2=SO2 | 0.012×1/3=0.004 | 0.004×32/320.004 | 0.004×64/32=0.008* |
S | [S]+(CaO)=CaO+[O] | 0.012×2/3=0.008 | 0.008×(-16)/32=-0.004 | 0.008×72/32=0.018 |
Fe | [Fe]+1/2O2=(FeO) | 0.782 | 0.782×16/56=0.223 | 1.006* |
Fe | 2[Fe]+3/2O2=(Fe2O3) | 0.033 | 0.033×48/112=0.014 | 0.047* |
总计 | 6.322 | 7.417 | ||
成分 | 质量,kg | 成分p m 2.5 | 质量,kg |
Fe2O3 | 1×61.80%=0.618 | FeO | 1×29.40%=0.294 |
SiO | 1×5.61%=0.0561 | Al2O3 | 1×1.10%=0.011 |
CaO | 1×1.0%=0.01 | MgO | 1×0.52%=0.005 |
S | 1×0.07%≈0.001 | H2O | 1×0.50%=0.005 |
成分 | 质量,kg | 成分 | 质量,kg |
CaF2 | 0.3×89.0%=0.267 | P | 0.3×0.55%=0.002 |
SiO | 0.3×6%=0.018 | S | 0.3×0.09%=忽略 |
Al2O3 | 0.3×1.78%=0.005 | H2O | 0.3×2%=0.006 |
MgO | 0.3×0.58%=0.002 | ||
成分 | 质量,kg | 成分 | 质量,kg |
CaO | 3.0×55%=1.65 | MgO | 3.0×33%=0.99 |
SiO2 | 3.0×3%=0.09 | Fe2O3 | 3.0×1%=0.03 |
Al2O3 | 3.0×3%=0.09 | 烧碱 | 3.0×5%=0.15 |
成分 | 质量,kg | 成分 | 质量,kg |
CaO | 0.5×54%=0.27 | SiO2 | 0.5×2%=0.01 |
MgO | 0.5×38%=0.19 | C | 0.5×5%=0.025 |
Al2O3 | 0.5×1%=0.09 | ||
成分 | 质量,kg | 成分 | 质量,kg |
CaO | 5.55×91%=5.05 | SiO | 5.55×2%=0.11 |
MgO | 5.55%×2%=0.11 | S | 5.55×0.05%=0.003 |
Al2O3 | 5.55×1.5%=0.08 | 烧碱 | 5.55×3.45%=0.19 |