项目 | 黑龙江省尼龙厂 | 上海塑料制品十八厂 | 江苏宜兴化工二厂 | |
I型 | II型 | |||
分子量 | (1.5~2)×104 | (1.5~2)×104 | (1.8~2.2)×104 | |
外观 | 乳白,微黄 | 乳白,微黄 | 白或带黄粒 | 乳白至淡黄 |
相对密度 | 1.10~1.15 | 1.10~1.15 | 1.10~1.14 | 1.13~1.15 |
粒度,粒/克,> | 40 | 40 | ||
含水量,%,≤ | 0.3 | 0.15 | 2 | |
粘度比 | 0.40~3.00 | >3.00 | ||
小黑点含量,%,≤ | 3 | 3 | ||
熔点,℃ | 238~248 | 238~248 | 255~260 | |
脆化温度,℃ | -35 | -35 | ||
马丁耐热,℃ | 50~60 | |||
拉伸强度,MPa | ≥65 | ≥70 | 60~80 | 70~80 |
弯曲强度,MPa | ≥100(不断) | ≥110(不断) | 100~120 | 80~120 |
弯曲弹性模量,GPa | 2~3 | |||
冲击强度,kJ/m2缺口 无缺口 | ≥8 | ≥10 | 60~100 | 8 ~12 |
硬度,MPa | R118 | |||
体积电阻率,Ω·cm | ≥1014 | ≥1014 | 1.830×1015 | |
介电常数(1MHz) | 1.63 | |||
成型收缩率,% | 1.5~2.2 | |||
指标 | 阻燃尼龙66 | 阻燃增强尼龙66 | 防老化尼龙66 | 玻纤增强尼龙66 |
汽车空调电磁离合器 熔点,℃ | 245~250 | 247~250 | 250~260 | |
相对密度 | 1.42~1.45 | 1.50 | 1.10~1.15 | 1.39 |
吸水率,% | <0.5 | ≤1.0 | ||
拉伸强度,MPa | ≥60 | 120 | ≥60 | ≥162 |
弯曲强度,MPa | ≥100 | 180 | ≥90 | ≥196 |
缺口冲击强度,kJ/m2 | ≥5 | 10 | ≥5 | ≥9.8 |
热变形温度(1.8MPa),℃ | 60 | 220 | 60 | ≥220 |
阻燃等级,UL94 | V-0 | V-0 | ||
体积电阻率,Ω·cm | ≥1015 | 1013 | ≥1.5×1015 | ≥1014 |
介电常数 | <5 | 5 | 4.4 | |
击穿电压,kV/mm | ≥17 | 17 | 20 | 20 |
模后收缩率,% | 0.5~1.2 | 0.5~1.0 | 0.8~1.5 | |
玻纤含量,% | 30±2 | 30±2 | ||
弯曲弹性模量,MPa | ≥5.4×103 | |||
耐老化性能,倍 | >3 | |||
表面电阻率,Ω | ≥1013 | |||
型号 | 用途 | |
Zytel 101L Zytel 101F Zytel 103HSL Zytel 103FHS Zytel 105F Zytel EFE1068 Zytel 135F | 增润PA66 快速成型 热稳定性增润尼龙66 快速成型热稳定性尼龙66 抗紫外线增润尼龙66 核化尼龙66 增润成核型尼龙66 | 机械零件、消费品等 |
增韧级 Zytel114BK97 Zytel408 Zytel450 Zytel490 | 抗冲改性PA66 增韧PA66 增韧PA66 增韧PA66 | 具优越的韧性和成型性 |
超韧级 ZytelST801 | 超韧PA66 | 杰出的耐冲击性 |
特制品 Zytel122L ZytelEFE8073 ZytelFN714 ZytelFN718 | 抗水解增润PA66 增韧PA66挤出级 PA66尼龙合金 PA66尼龙合金 | |
玻纤增强 Zytel70G20HSL Zytel70G25HSL Zytel70G30HSL Zytel70G35HSL Zytel70G43HSL Zytel70G50HSL Zytel70G60HSL | 20%GF,热稳定性增润PA66 25%GF,热稳定性PA66 30%GF,热稳定性PA66 35%GF,热稳定性PA66 43%GF,热稳定性PA66 50%GF,热稳定性PA66 60%GF,热稳定性PA66 | |
抗水解玻纤增强级 Zytel70G25HSLR Zytel70G30HSLR Zytel70G30HSR2 | 25%GF,热稳定性增润抗水解PA66 30%GF,热稳定性增润抗水解PA66 30%GF,热稳定性增润超高抗水解性能PA66 | |
玻纤增强特制品级 Zytel70G33GRA Zytel70G35HSLX Zytel70G35HSLRA4 Zytel70GB40HSL ZytelEFE7267 Zytel74G20HSL Zytel74G30L Zytel70G30W | 玻纤增强增润PA66 35%GF,抗热油脂性PA66 高流动性玻纤增强PA66 40%GF,热稳定性PA66 可焊接性玻纤增强PA66 20%GF,热稳定性PA66/6共混 20%GF,PA66/6共混 玻纤增强耐侯性PA66/6共混 | |
增韧玻纤增强级 Zytel79G13L Zytel80G14 Zytel80G25 Zytel70G33HS1R | 13%GF,增韧PA66 14%GF,增韧PA66 25%GF,增韧PA66 35%GF,热稳定性增韧PA66 | |
阻燃级 ZytelFR7200V0F ZytelFR72G25V0 ZytelFR70G25GW ZytelFR70G25V0 ZytelFR70M30V0 ZytelFR70M40GW | 未增强PA66/6共聚物,UL94V-0(0.5mm) 25%GF PA66/6共聚物,UL94V-0(0.5mm) 25%GFPA66,炽热棒850℃(1mm) 25%GF,PA66,UL94V-0(0.5mm) 30%矿物增强PA66,UL94V-0(1.6mm) 40%矿物增强,炽热棒960℃(1.5mm) | |
高粘挤出级 ZytelE40 ZytelE42A ZytelE50 ZytelE51HSB ZytelE53 | 高粘PA66(RV=95~150) 高粘PA66(RV=180~310) 高粘PA66(RV=240~270) 热稳定性高粘PA66(RV=240~470) 高粘PA66(RV=470~600) | 长条状、管状以及其它复杂成型品挤出用,或用于耐冲击之成型品 |
密度 | 阻燃性 | 吸水率 | 吸湿率 | 洛氏硬度 | 落球冲击硬度 | 成型收缩率 | |||
测试条件 | 1.6mm | 23℃,饱和 | 23℃50%RH | M | R | 流动方向 | |||
标准ISO | 1183 | UL94 | ISO 62 | 2039/2 | 2039 | 294-4 | |||
单位 | g/cm3 | % | MPa | % | |||||
101L,DAM 50%RH | 1.14 | V-2 | 电子标签生产设备8.5 | 2.8 | 79 59 | 121 108 | 160H961/30 85 H358/30 | 1.3 | |
101F,DAM 50%RH | 1.14 | V-2 | 8.5 | 2.8 | 1.3 | ||||
103HSL,DAM 50%RH | 1.14 | V-2 | 8.5 | 2.8 | 1.3 | ||||
103FHS,DAM 50%RH | 1.14 | V-2 | 8.5 | 2.8 | 1.3 | ||||
105F,DAM | 1.14 | V-2 | 8.5防盗追踪 | 2.8 | 1.5 | ||||
EFE1068,DAM 50%RH | 1.14 | V-2 | 8.5 | 2.8 | |||||
135F,DAM 50%RH | 1.14 | V-2 | 8.5 | 2.7 | 87 64 | 123 116 | 0.7 | ||
408,DAM 50%RH | 1.09 | HB | 7 | 2.2 | 71 50 | 115 102 | 1.5 | ||
450,DAM 50%RH | 1.08 | HB | 7 | 2.2 | 1.8 | ||||
490,DAM 50%RH | 1.08 | HB | 7.1 | 2.3 | 1.6 | ||||
801,DAM 50%RH | 1.08 | HB | 6.7 | 2.2 | 112 89 | 1.7 | |||
EFE8073,DAM 50%RH | 1.07 | ||||||||
70G20HSL,DAM 50%RH | 1.29 | HB | 6.8 | 2.1 | 102 85 | 122 115 | 0.4 | ||
70G35HSL,DAM 50%RH | 1.41 | HB | 5.5 | 1.7 | 105 89 | 125 117 | 285 203 | 0.3 | |
70G60HSL,DAM 50%RH | 1.70 | HB | 3.4 | 1.0 | 0.2 | ||||
70G25HSLR,DAM 50%RH | 1.33 | HB | 6.4 | 2.0 | 0.3 | ||||
70GB40HSL,DAM 50%RH | 1.46 | HB | 7.3 | 1.7 | 1.3 | ||||
80G14,DAM 50%RH | 1.18 | HB | 6.2 | 2.0 | 103 | 0.4 | |||
FR7200V0F,DAM 50%RH | 1.19 | V-0 | 6.4 | 2.6 | 1.2 | ||||
FR72G25V0,DAM 50%RH | 1.49 | V-0 | 4.1 | 1.1 | 213 106 | 0.2 | |||
E40,DAM 50%RH | 1.14 | 2.6 | 1.5 | ||||||
E42A,DAM 50%RH | 1.14 | HB | 8.5 | 2.6 | 1.5 | ||||
屈服 应力 | 屈服 应变 | 断裂 应变 | 标称断 裂应变 | 拉伸 模量 | 冲击强度 (无缺口) | 缺口冲击强度 | |||
测试条件 | 50mm/min | 1mm/min | 23℃ | -30℃ | 23℃ | -30℃ | |||
标准ISO | 527-1/2 | 179/1eU | 180/1A | ||||||
单位 | % | % | % | MPa | kJ/m2 | kJ/m2 | |||
101L,DAM 50%RH | 83 53 | 4.5 25 | 40 >50 | 22 >50 | 3100 1200 | NB NB | NB NB | 5.4 11.7 | 3.7 2.7 |
101F,DAM 50%RH | 83 53 | 4.4 25 | 40 >50 | 18 >50 | 3100 1200 | NB NB | NB NB | 5.4 11.7 | 3.7 2.7 |
103HSL,DAM 50%RH | 85 53 | 4.4 25 | 40 >50 | 18 >50 | 3100 1250 | NB NB | NB NB | 5 10.6 | 2.8 3.1 |
103FHS,DAM 50%RH | 85 55 | 4.4 25 | 35 >50 | 18 >50 | 3100 1350 | NB NB | NB NB | 5 10 | |
105F,DAM 50%RH | 85 60 | 5 25 | 30 >50 | 24 >50 | 3200 1500 | 45 NB | 55 55 | 5 4 | 12 3 |
EFE1068,DAM 50%RH | 85 59 | 4.5 25 | 35 >60 | 18 >60 | 3100 1500 | NB NB | 5 11.5 | ||
135F,DAM 50%RH | 98 69 | 4.5 18 | 18 >50 | 13 >50 | 3600 2100 | NB NB | NB NB | 3 2.8 | |
408,DAM 50%RH | 61 43 | 6 26 | 55 >100 | 35 >50 | 2200 1100 | NB NB | NB NB | 19 20 | 11 4 |
450,DAM 50%RH | 55 40 | 5.4 24 | 50 >100 | 28 >50 | 2200 1000 | NB NB | NB NB | 17 70 | 10 9 |
490,DAM 50%RH | 55 40 | 5.5 29 | 50 >100 | 33 >50 | 2100 950 | NB NB | NB NB | 66 83 | 17 16 |
801,DAM 50%RH | 50 40 | 6 38 | 40 >50 | 60 >100 | 2000 900 | NB NB | NB NB | 80 100 | 20 20 |
EFE8073,DAM 50%RH | 52 37 | 5.5 32 | 50 >100 | 88 >100 | 2000 950 | NB NB | 75 93 | 16 15波盘 | |
70G20HSL,DAM 50%RH | 159 103 | 2.8 7 | 7200 5300 | 54 69 | 50 43 | 10 11 | 8 8 | ||
70G35HSL,DAM 50%RH | 210 155 | 3.2 4 | 11500 8900 | 98 100 | 88 77 | 12 15 | 10 10 | ||
柴火无烟灶70G60HSL,DAM 50%RH | 230 180 | 1.6 2.1 | 20000 15000 | 74 80 | 60 58 | 12 9.5 | 8 7.5 | ||
70G25HSLR,DAM 50%RH | 188 115 | 3 15 | 8600 6300 | 50 60 | 60 45 | ||||
70GB40HSL,DAM 50%RH | 90 43 | 6 13 | 5000 2700 | 30 40 | 25 25 | 3.5 6.5 | 2.8 2.8 | ||
80G14,DAM 50%RH | 110 70 | 4 10 | 5100 3400 | 75 电脑加密锁75 | 85 90 | 14 19 | 7 7 | ||
FR7200V0F,DAM 50%RH | 85 50 | 4 20 | 3900 1800 | 50 NB | 65 65 | 3 8 | 3 3 | ||
FR72G25V0,DAM 50%RH | 135 100 | 2.5 3.5 | 9200 6500 | 55 62 | 70 61 | 9 12 | 8 8 | ||
E40,DAM 50%RH | 85 55 | 4.4 28 | 50 >50 | 3000 1200 | NB NB | NB NB | 5.6 12.5 | 3 2.2 | |
E42A,DAM 50%RH | 86 52 | 5 27 | >50 >50 | 3100 1200 | NB NB | NB NB | 5.6 11.9 | 4.3 4 | |