HEAT RESISTANCE 耐热必 | Melting point:Hook230.c,Loop 180.c Maintains normal bonding performance during 1000 hours |
COLD RESISTANCE 耐寒性 | Still work when temperature is-20.c,and the lower the temperature is,the laiger the strength becomes,but with a decrease in durability.-20℃ 仍可使用,越低温拉力越强,但耐久性降. |
WATER RESISTANCE 耐水性 | Retains 50% of closure strength in water and recovers 100% of strength a fter |
CHEMICALS RESISTANCE 耐药性 | Alkali:Within 50% ofAIkaline sODA.within28% ofammonia. Acid:Within 2.5% of Hydrochloric Acid,15% of Sulphuric Acid,and 2.5% of Nitric Acid. 碱性苏打50%,氨28%,盐酸2.4%,硝酸3.5%以下仍能发挥功效. |
WHEEL CYCLE使用次数 \ 钼板坯STRENGTH测试项目 | PEEL STRENGTH 剥离强度(G/CN) | SHEAR STRENGTH 横向拉力(G/CM2) |
ORIGINAL(使用前) | 250+ | 850+ |
1000TIMES(次) | 215+ | 740+ |
3000TIMES(次) | 182+ | 688+ ingan |
氨苄西林颗粒5000TIMES(次) | 165+ | 637+ |
Item 测试项目 | Rusel结果 | Method测试方法 | |
Againstlight 耐水牢度 | Change变褪 | Grade3+(3级以上) | CNS-1493或JIS-L-0842 |
Change变褪 | Grade4+(4级以上) | ||
Against Washing 耐水牢度 | Stain污 | Grade3+(3级以上) | CNS-1493或JIS-L-0842 A-4号 |
Change变褪 | Grade4+(4级以上) | ||
Against Hot Water磨具制造 耐热水洗牢度 | Stain污 | Grade3+(3级以上) | CNS-1495或JIS-L-0842 3号 |
Change变褪 | Grade5+(5级以上) | ||
Against Sweat 耐汗牢度 | Stain污 | Grade4+(4级以上) | CNS-1496或JIS-L-0842 C法 |
Change变褪 | Grade4+(4级以上) 功率分配器 | ||
Against Rubbding 耐摩擦牢度 | Stain污 | Grade4+(4级以上) | CNS-1499或JIS-L-0842 Ti型 |
1、BS7271(U.K)英国 2、FEDD-STD-191(U.S.A)美国 3、CBS(TAIWAN)台湾 4、JIS-L-1086(JAPAN)日本 |