钢帘线结构 | 捻距 (±5%) mm | 捻向 | 粗度 (±5%) mm | 最小破断力 (±5%) N | 破断伸长率 (±1.5%) % | 线密度 (±5%) g/m |
2+1×0.28 | ∞/16 | -S | 0.700 | 470 | 1.470 | |
2+2×0.28 | ∞/16 | -S | 0.730 | 625 | 1.940 | |
pcu h2+2×0.30 | ∞/16 | -S | 0.780 | 700 | 2.230 | |
4×0.25 OC | 14 | S | 0.640 | 520 | 1.550 | |
5×0.25 | 10 | S | 0.670 | 660 | 1.950 | |
2+7×0.22 | 6.3/12.5 | SS | 0.830 | 920 | 2.740 | |
2+7×0.28+0.15 | 8/16/5 | SSZ 钢帘线 | 1.330 | 1370 | 4.640 | |
3×0.20+6×0.35 | 10-18 | SZ | 1.130 | 1590 | 5.340 | |
12×0.22+0.15 CC | 12.5/3.5 | SZ | 1.180 | 1200 | 3.840 | |
3×0.22/9×0.20 CC | 12.5 | S | 0.88 | 1060 | 3.170 | |
3+9×0.22 | 6.3/12.5 | SS | 0.920 | 1200 | 3.650 | |
0.20+18×0.20 CC | 12.5 | Z | 1.020 | 1620 | 4.840 | |
3+9+15×0.175+0.15 | 5/10/16/3.5 | SSZS | 1.340 | 1720 | 5.420 | |
3+9+15×0.22+0.15 | 6.3/12.5/18/3.5 | SSZS | 1.620 | 2700 | 8.500 | |
2+1×0.28 HT | ∞/16 | -S | 0.700 | 535 | 1.470 | |
2+2×0.30 HT | ∞/16 | -S | 0.780 永磁同步电机反电动势 | 800 | 2.230 | |
3+2×0.35 HT | 干衣柜∞/18 | -S | 1.070 | 1310 | 3.820 | |
2+7×0.20+0.15 HT | 5.6/11.2/3.5 | SSZ | 1.030 | 870 | 2.440 | |
3×0.20+6×0.35 HT | 10/18 | SZ | 1.130 | 1820 | 5.340 | |
12×0.22 HT | 12.5 | S | 0.910 | 1410 | 3.640 | |
3×0.22/9×0.20 CC HT | 12.5 | S | 0.880 | 1220 | 3.170 | |
3+9×0.175+0.15 HT | 5/10/3.5 | SSZ | 1.000 | 890 | 2.490 | |
3+9×0.25 HT | 7/14.5 | SS | 1.020 | 1750 | 4.710 | |
3+8×0.33 HT | 10/18 | SS | 1.380 | 2530 | 7.550 | |
0.20+18×0.20 CC HT | 12.5 | Z | 1.020 | 1860 | 4.840 | |
3×4×0.22 HE | 3.15/6.3 | SS | 1.180 | 940 | 5.5 | 3.950 |
4×4×0.22 HE | 3.5/5 | SS | 1.320 | 1260 | 5.5 | 5.400 |
3×6×0.22 HE | 3.5/6.3 | SS | 1.500 | 1410 | 6.5 | 6.050 |
3×7×0.20 HE | nnn163.9/6.3 | SS | 1.390 | 1360 | 6.5 | 5.850 |
3×7×0.22 HE | 4.5/8 | SS | 1.520 | 1650 | 6.5 | 6.950 |
检验方法 | GB/T 11181-2003 | |||||
镀层种类 | 普通镀层 | 低铜镀层 | 检验方法 | ||||
单丝直径 mm | ﹤0.20 | 0.20 ~ 0.30 | ﹥0.30 | ﹤0.20 | 0.20 ~ 0.30 | ﹥0.30 | YB/T135 |
镀层中铜含量 % | 67.5±2.5 | 63.5±2.5 | |||||
镀层厚度 μm | 0.20±0.06 | 0.24±0.06 | 0.30±0.06 | 0.20±0.06 | 0.24±0.06 | 0.30±0.06 | |