序号 | 材料状态 | 材料牌号及标准 | 规格（mm） | 化学成分（%） | |||||||||
C | Si | Mn | P | S | Cr | Ni | Mo | V | 其它 | ||||
1 | 不 锈 钢 棒 | 0Cr13 GB/T1220 | Φ30~70×500 | ≤0.08 | ≤1.00 | ≤1.00 | ≤0.040 | ≤0.030 | 11.50~13.00 | ≤0.60 | |||
2 | 1Cr13 GB/T1220 | 0.08~0.15 | ≤1.00 | ≤1.00 | ≤0.040 | ≤0.030 | 11.50~13.00 | ≤0.60 | |||||
3 | 1Cr11MoV GB/T1221 | 0.11~0.18 | ≤0.50 | ≤0.60 | ≤0.035 | ≤0.030 | 10.00~11.50 | ≤0.60 | 0.50~0.70 | 0.25~0.40 | |||
4 | 10 GB/T699 | 0.07~0.13 | 0.17~0.37 | 0.35~0.65 | ≤0.035 | ≤0.035 | ≤0.15 | ≤0.30 | Cu≤0.25 | ||||
5 | 20 GB/T699 | 0.17~0.23 | 0.17~0.37 | 0.35~0.65 | ≤0.035 | ≤0.035 | ≤0.25 | ≤0.30 | Cu≤0.25 | ||||
6 | 25 GB/T699 | 0.22~0.29 | 0.17~0.37 | 0.35~0.65 | ≤0.035 | ≤0.035 | ≤0.25 | ≤0.30 | Cu≤0.25 | ||||
7 | 30 GB/T699 | 0.27~0.34 | 0.17~0.37 | 0.35~0.65 | ≤0.035 | ≤0.035 | ≤0.25 | ≤0.30 | Cu≤0.25 | ||||
8 | 35 GB/T699 | 0.32~0.39 | 0.17~0.37 | 0.35~0.65 | ≤0.035 | ≤0.035 | ≤0.25 | ≤0.30 | Cu≤0.25 | ||||
9 | 45 GB/T699 | 0.42~0.50 | 0.17~0.37 | 0.50~0.80 | ≤0.035 | ≤0.035 | ≤0.25 | ≤0.30 | Cu≤0.25 | ||||
10 | 35Mn GB/T699 | 0.32~0.39 | 0.17~0.37 | 0.70~1.00 | ≤0.030 | ≤0.030 | ≤0.25 | ≤0.30 | Cu≤0.25 | ||||
11 | 不 锈 钢 废 料 | 0Cr19Ni9 卷料 GB/T4223 | GB/T4223 | ≤0.08 | ≤2.00 | ≤1.50 | ≤0.03 | ≤0.03 | 16~20 | 6~11 | |||
12 | 1Cr13卷料GB/T4223 | GB/T4223 | ≤0.15 | ≤0.60 | ≤0.60 | ≤0.03 | ≤0.03 | 11.00~14.50 | ≤0.60 | ||||
13 | 1Cr17卷料GB/T4223 | GB/T4223 | ≤0.15 | ≤0.60 | ≤0.60 | ≤0.03 | ≤0.03 | 16.00~19.00 | ≤0.60 | ||||
14 | 合 金 炉 料 合 金 炉 料 | 电解镍 GB/T6516 Ni9996 | 20~40 ×20 | ≤0.10 | ≤0.002 | ≤0.001 | ≤0.001 | ≥99.96 | Co≤0.02 | ||||
15 | 微碳铬铁 GB/T5683 FeCr55C0.03 | 单块重量4±1Kg，料块尺寸：120×200其余GB/T5683 | 0.03 | ≤1.50 | ≤0.03 | ≤0.03 | ≥55.00 | ||||||
16 | 金属铬GB/T321 JCr99A | GB/T321 | 无机砂浆≤0.01 | ≤0.25 | ≤0.005 | ≤0.01 | ≥99.00 | ||||||
17 | 氮化铬YB/T5140 FeNCr6-B | 5~10 Kg/块 其余YB/T5140 | ≤0.06 | ≤2.50 | ≤0.03 | ≤0.04 | ≥60.00 | N≥5.00 | |||||
18 | 金属锰GB/T2774 JMn97 | GB/T2774 | ≤0.08 | ≤0.40 | ≥97.00 | ≤0.04 | ≤0.04 | ≤0.02 | Cu≤0.03 Al+Ca+Mg≤0.70 | ||||
19 | 纯铁 GB/T9971 YT1 | GB/T9971 | ≤0.010 | ≤0.06 | ≤0.20 | ≤0.015 | ≤0.012 | ≤0.02 | ≤0.02 | Cu≤0.10 Al≤0.50 | |||
20 | 硅铁 GB/T2272 FeSi75-A | GB/T2272 | ≤0.10 | 74.0~80.0 | ≤0.40 | ≤0.035 | ≤0.02 | ≤0.30 | |||||
21 | 锰铁GB/T3795 FeMn88C0.2 | GB/T3795 | ≤0.20 | ≤2.00 | 85.0~92.0 | ≤0.10 | ≤0.02 | ||||||
22 | 钼铁GB/T3649 FeMo60-B | 钢舌鼓GB/T3649 | ≤0.10 | ≤1.50 | ≤0.05 | ≤0.10 | 60.0~65.0 | ||||||
23 | 硅钙合金YB/T5051 Ca31Si60 | YB/T5051 | ≤1.20 | 50.0~65.0 | ≤0.04 | ≤0.06 | rat组合 | Ca≥31 Al≤2.4 | |||||
24 | 铸造生铁 GB/T 718 Z14 | GB/T 718 | ≥3.30 | 1.25~1.60 | ≤0.5 | ≤0.060 | ≤0.030 | ||||||
25 | 纯铝 GB/T1196 | Φ10×1000 | ≤0.13 | Al≥99.7 | |||||||||
名称 | 牌号 | 化学成分 % | |||||
MgO | CaO | SiO2 | Fe2O3 | Al2O3 | |||
电熔镁砂 | FM980 | ≥98.0 | ≤1.2 | ≤0.6 | ≤0.6 | ≤0.2 | ≥3.5 |
化学成分% | CaO+MgO | ≥55 |
SiO2 | <20 | |
Al2O3 | <12 | |
自然堆积密度g/cm3 | 0.8 | |
膨胀后堆积密度g/cm3 | 0.3~0.4 | |
膨胀温度℃ | 1500~1550 | |
名称 | 牌号 | 化学成分 % | |||
Al2O3+ SiO2 | Al2O3 | Fe2O3 | K2O+Na2O | ||
普通硅酸铝耐火纤维毡 | STD | ≥96.0 | ≥45.0 | ≤1.2 | ≤0.5 |
指标/材质 | 平均参考尺寸(mm) | 名义重量（Kg） | |||
外径 | 内径 | 外高 | 内高 | ||
M-9 | 130 | 106 | 225 | 200 | 9.5 |
M-14 | 160 | 130 | 225 | 210 | 15 |
MA-14 | |||||
M-25 | 175 | 140 | 325 | 300彩油泥 | 25 |
MA-25 | |||||
M-100 | 245 | 205 | 520 | 460 | 120 |
MA-100 | |||||
MgO % | SiO2 % | Al2O3 % | CaO % | Fe2O3 % | 常温耐压强度 Mpa | 显气孔率 % | 热膨胀系数20~1300℃ | 耐急冷急热次数1200℃风冷 | 体积密度 g/cm3 pvc再生颗粒 | 最高工作温度℃（0.13Pa） | |
MgO | ≥94.0 | ＜2.0 | ＜0.5 | ≤2.0 | ≤0.8 | ≥1.96 | 14.0~19.0 | ＜13×10-6 | ＞20 | 2.9~3.1 | 1650 |
MgO-Al2O3 | 67.8~88.0 | ＜2.5 | 8.5~27.0 | ≤2.5 | ≤加密存储0.8 | ＞14.7 | 18.0~22.0 | ＜9×10-6 | ＞40 | 2.8~3.0 | 1650 |
本文发布于:2024-09-22 15:28:18，感谢您对本站的认可！
本文链接：https://www.17tex.com/tex/3/178726.html
版权声明：本站内容均来自互联网，仅供演示用，请勿用于商业和其他非法用途。如果侵犯了您的权益请与我们联系，我们将在24小时内删除。
| 留言与评论（共有 0 条评论） |
豫公网安备41160202000603
站长QQ:729038198
关于我们
投诉建议