(中国瑞林工程技术股份有限公司，江西南昌330038) 〔摘要〕以西南某冶炼厂300kt/a改扩建项目为例，从工艺指标、投资指标、技术经济指标等方面对富氧侧吹+多喷顶吹连续炼铜工艺和闪速熔炼+闪速吹炼工艺进行了对比分析，论证得出两种方案工艺指标各有优势，但从投资、技术经济指标上看，野侧+顶冶工艺比野双闪冶工艺更适合该厂的扩建。wsrd
导电橡胶片〔关键词〕技改扩建；连续炼铜；富氧侧吹；双闪
中图分类号:TF111.1文献标志码：B文章编号：1004-4345(2020)05-0006-03
Comparative Study on Technical Upgrading and Expansion of a Copper Smelter in Southwest China
XIONG Jiaqiang,LIU Yang
(China Nerin Engineering Co.,Ltd.,Nanchang,Jiangxi330038,China)
Abstract Taking a300kt/a smelter reconstruction and expansion project in the southwest as an example,the paper makes a comparative analysis of oxygen enriched side blowing+multi-lance top-blowing continuous copper smelting process and flash smelting+flash converting process from the aspects of process index,investment index and technical and economic index.It is proved that the two schemes have their own advantages,however,the"side+top"process is more suitable for the smelter expansion than the "double flash"process from the investment and technical and economic indicators.
Keywords technical upgrading and expansion;continual copper smelting;oxygen enriched side blown;double flash smelting; competitiveness
随着近年来铜冶炼技术的高速发展，能够实现大型化、连续化、清洁化的冶炼技术得到了大规模应用。富氧侧吹+多喷顶吹连续炼铜工艺（以下简称“侧+顶”工艺）与闪速熔炼+闪速吹炼工艺（以下简称双闪工艺），因其具有规模化效应及环保优势，已成为铜冶炼发展的主流方向，是近十年最具先进性和代表性的铜冶炼工艺典范。
“侧+顶”工艺是我国自主开发的连续炼铜技术。侧吹熔炼过程中，高浓度的富氧空气通过炉体侧部的风口吹入炉渣层进行强氧化反应。熔炼产生出高品位的冰铜通过溜槽流入顶吹吹炼炉。顶吹吹炼技术采
用多喷将富氧空气送入炉内熔体中发生吹炼反应，吹炼形成的粗铜沉入炉体下部通过虹吸口连续放出，再通过溜槽流入阳极铜中进一步精炼。该工艺熔炼强度高，单位生产能力大，单炉最大年产能已达到300kt粗铜［1-2］。且该熔炼技术原料适应性强，不需要进行原料预处理。熔炼、吹炼和精炼工艺均通过溜槽连接，避免了含硫烟气无组织排放及吊车倒运的安全问题。目前，该工艺已成功应用于中国瑞林工程技术股份有限公司（以下简称“中国瑞林”）设计的南国冶炼厂、赤峰云铜冶炼厂、刚果（金）卢阿拉巴冶炼厂等新建冶炼厂，总产能已接近1000kt/a阴极铜。
双闪工艺最早应用于美国肯尼科特冶炼厂，已投产近30年，引入国内也已应用10余年。该工艺的技术原理属于悬浮熔炼，铜精矿或铜锍从炉顶喷嘴通过反应塔落入沉淀池，在反应塔下落的空中完成杂质的氧化反应。该工艺的主要优势在于冶炼强度大、无SO2低空污染问题、SO2烟气浓度高、炉体寿命