DOI ：lO. 13979/j. 1007-7235.2019.05.0067075铝合金¢482 mm 铸锭热顶铸造工艺试验研究 赵 扬，寇明珠，孙庆福，杨松渝，吕 鑫，黄 博
(东北轻合金有限责任公司，黑龙江哈尔滨150060)
摘要：为满足市场对大规格髙强度铝合金材料的需求，对7075铝合金0482 mm 圆铸锭的热顶铸造工艺进行试验研 究。从原料选用、成分调整、熔炼温度控制、导炉、铸造工艺参数等多个环节进行控制，制得表面光滑的铸锭。对铸 锭取样进行化学成分分析和低、高倍组织检查，结果表明热顶铸造制得的铸锭表面质量、内部组织、化学成分偏析情 况比传统铸造方法均有改善，更能满足用户的要求。
关键词：大直径7075铝合金铸锭；热顶铸造；熔铸工艺；质量分析
中图分类号:TG292 文献标识码：A 文章编号：1007 - 7235 ( 2019 ) 05 - 0034 - 04
Experimental research on the hot-top casting process
for ¢482 mm ingots of 7075 aluminum alloy
ZHAO Yang,K0U Ming-zhu,SUN Qing-fu,YANG Song-yu,LV Xin,HUANG Bo
(Northeast Light Alloy Co. ,Ltd. ,Harbin 150060,China)
Abstract : To meet the market demand for large-sized high-strength aluminum alloy materi als ,the hot top casting experimental research was carried out on ①482mm 7075 aluminum alloy billet. The billet with smooth surface was made by controlling the raw material selec tion ,composition adjustment , melting temperature control , molten metal transfer and casting process parameters and soon. Chemical composition analysis and low and high magnification structure examination were performed on the billet samples. The results show that the surface quality , internal structure and chemical composition segregation of the billet made by hot-top casting are improved compared with the traditional casting method and can meet the require ments of customers better.
Key words : large-diameter 7075 aluminum alloy billet ；hot top casting ；melting and cast ing process ; quality analysis
7xxx 铝合金是航空、航天工业用的重要材料之
一。随着用户对材料品质要求越来越高，铝加工行 业内对7xxx 铝合金铸锭质量的要求也更加严格。
在这样的情况下采用热顶铸造工艺替代传统铸造方 式的趋势越发明显。热顶铸造有以下优点⑴：①石墨环润滑作用好、
一次水冷结晶区域窄，能促进铸锭表面质量提升，有 效控制铸锭拉裂、夹渣等表面缺陷;②热顶结晶器的 有效结晶高度很小，铸造冷却速度快，使铸锭的晶内 结构更为细薄，也使铸造时的液穴变浅、过渡带变
窄，因而铸锭致密度提高，化学成分沿铸锭截面的分
布更为均匀;③热顶铸造水平供流方式液面稳定性收稿日期：2018-11 -20
第一作者简介：赵扬（1991 -），男，齐齐哈尔人，助理工程师
。