冷轧产品相近牌号对照表(1)-低碳钢 | ||||||||||||
标准号 | Q/BQB 402-2003 | Q/BQB 403-2003 | Q/BQB 408-2003 | JIS G3141-1996 | JFS A2001-1998 | EN 10130-1999 | DIN 1623-(1)-1983 | ASTM A1008-02e1 | GB/T 5213-2001 | ISO 3574-1999 | ||
牌 号 | SPCC | DC01(St12) | BLC | SPCC | JSC270C | DC01 | St12 | CS | - | CR1 | ||
SPCD | DC03(St13) | BLD | SPCD | JSC270D | DC03 | RRSt13 | DS | - | CR2 | |||
SPCE | DC04(St14,St15) | BUSD | SPCE | JSC270E | DC04 | St14 | DDS | SC1 | CR3 | |||
SPCEN | DC05(BSC2) | BUFD | SPCEN | JSC270F | DC05 | - | EDDS | SC2 | CR4 | |||
- | DC06 (St16,St14-T BSC3) | BSUFD | - | JSC260G | DC06 | - | - | SC3 | CR5 | |||
冷轧产品相近牌号对照表(2)-加磷钢 | ||||||||||||
标准号 | Q/BQB 411-2003 | JFS A2001-1998 | JIS G3135-1986 | prEN 10268-2002 | ||||||||
牌 号 | B170P1 | JSC340P | SPFC340 | - | ||||||||
B210P1 | JSC390P | SPFC390 | - | |||||||||
B250P1 | JSC440P | SPFC440 | - | |||||||||
B180P2(BP340) | JSC340W | - | H180P | |||||||||
B220P2(BP380) | JSC390W | - | H220P | |||||||||
冷轧产品相近牌号对照表(3)-烘烤硬化钢 | ||||||||||||
标准号 | Q/BQB 416-2003 | JFS A2001-1998 | JIS G3135-1986 | prEN 10268-2002 | ||||||||
牌 号 | B140H1 | JSC270H | - | - | ||||||||
B180H1 | JSC340H | - | - | |||||||||
B180H2(BH340) | - | SPFC340H | H180B | |||||||||
冷轧产品相近牌号对照表(4)-双相钢 | ||||||||||||
标准号 | Q/BQB 418-2003 | JFS A2001-1998 | SAE J2340-1999 | |||||||||
牌 号 | B240/390DP | - | - | |||||||||
B280/440DP在线升级 | - | - | ||||||||||
B340/590DP | JSC590Y | 600DL1 | ||||||||||
B400/780DP | JSC780Y | - | ||||||||||
冷轧产品相近牌号对照表(5)-低合金高强钢 | ||||||||||||
标准号 | Q/BQB 419-2003 | JFS A2001-1998 | SAE J2340-1999 | prEN 10268-2002 | ||||||||
牌 号 | B340LA | JSC440R | 340X | H340LA | ||||||||
B410LA | JSC590R | - | H420LA | |||||||||
用 途 | 牌 号 |
一般用 冲压用 深冲用 特深冲用 超深冲用 | St12 St13 St14 St15 St14-T |
牌 号 | 脱氧方式 | 化 学 成 分 % | |||||
C | Si | Mn | P | S | Alt | ||
St12 St13 St14 St14-T St15 | 铝镇静 铝镇静 铝镇静 铝镇静 铝镇静 | ≤0.10 ≤0.08 ≤0.080 ≤0.080 ≤0.06 | - - - - ≤0.03 | ≤0.50 ≤0.45 ≤0.40 ≤0.40 ≤0.35 | ≤0.035 ≤0.030 ≤0.020 ≤0.020 ≤0.020 | ≤0.035 ≤0.035 ≤0.030 ≤0.030 ≤0.025 | - - ≥0.025 ≥0.025 0.025~0.07 |
牌 号 | 拉 伸 性 能 | 硬 度 ② | ||||
屈服点 ① MPa 不大于 | 抗拉强度 MPa | 伸长率 % 不小于 | HRB | HRF | HR30T | |
不大于 | ||||||
St12 | 280 | 270~410 | 28 | 65 | 94 | 60 |
St13 | 240 | 270~370 | 34 | 55 | 88 | 53 |
St14 | 210 | 270~350 | 38 | 50 | 86 | 50 |
St14-T ③ | 210 | 270~350 | 42 | 50 | 86 | 50 |
St15 | 195 | 250~330 | 40 | - | 清理废旧钢筋- | - |
注:①屈服点为σSL或σP0.2 。 HR30T适用于厚度不大于0.6mm的钢板及钢带。 ③St14-T适用于特殊用户,加报r值、n值,最大供货宽度为1620mm。 | ||||||
杯突值 牌 号 公称厚度 | 冲 压 深 度 不小于 | |||||
St12 | St13 | St14、St14-T | kv7 St15 | |||
F | HF | ZF | ||||
0.5 | 8.8 | 9.5 | 9.6 | 9.7 | 9.8 | |
0.6 | 9.0 | 9.8 | 9.8 | 9.9 | 10.0 | |
0.7 | 9.2 | 10.0 | 10.1 | 10.2 | 10.3 | |
0.8 | 9.4 | 10.2 | 10.3 | 10.5 | 10.6 | |
0.9 | 9.6 | 10.3 | 10.5 | 10.7 | 10.8 | |
1.0 | 9.8 | 手机座充10.5 | 10.7 | 10.8 | 11.2 | |
1.1 | 9.9 | 10.7 | 10.9 | 11.0 | 11.3 | |
1.2 | 10.1 | 10.8 | 11.1 | 11.2 | 11.5 | |
1.3 | 10.2 | 11.0 | 11.2 | 11.3 | 11.7 | |
1.4 | 10.4 | 11.1 | 11.4 | 11.4 | 11.8 | |
1.5 | 10.5 | 11.2 | 11.5 | 11.6 | 12.0 | |
1.6 | 10.6 | 11.3 | 11.6 | 11.8 | - | |
1.7 | 10.7 | 11.5 | 11.7 | 12.0无烟抛光剂 | - | |
1.8 | 10.8 | 11.6 | 11.8 | 12.1 | - | |
1.9 | 11.0 | 11.7 | 11.9 | 12.2 | - | |
2.0 | 11.1 | 11.8 | 12.1 | 12.3 | - | |
注:①中间厚度钢板及钢带的杯突值,按表列值用内插法求出并修约至小数一位。 ②表列数值适用于三次试验结果的平均值,三个试验值中任一值低于规定平均值的数不得大于0.3mm。 | ||||||
冷连轧钢板及钢带的尺寸、外形、重量及允许偏差 | ||||||
Q/BQB 401-1999 代替 Q/BQB 401-94 | ||||||
公 称 厚 度 | 厚 度 允 许 偏 差 mm | |||||
高级精度 PT.B | 普通精度 PT.A | |||||
公 称 宽 度 | 公 称 宽 度 | |||||
<1200 | ≥1200~<1500 | ≥1500 | <1200 | ≥1200~<1500 | ≥15 00 | |
≥0.30~≤0.40 >0.40~≤0.60 >0.60~≤0.80 >0.80~≤1.00 >1.00~≤1.20 >1.20~≤1.60 >1.60~≤2.00 >2.00~≤2.50 >2.50~≤3.0 >3.0~≤3.5 | ±0.025 ±0.035 ±0.045 ±0.05 ±0.06 ±0.07 ±0.08 ±0.10 ±0.11 ±0.14 | ±0.035 ±0.045 ±0.05 ±0.06 ±0.07 ±0.08 ±0.09 ±0.11 ±0.12 ±0.15 | - ±0.05 ±0.05 ±0.06 ±0.07 ±0.08 ±0.09 ±0.11 ±0.12 ±0.15 | ±0.04 ±0.05 ±0.06 ±0.07 ±0.08 ±0.10 ±0.12 ±0.14 ±0.16 ±0.17 | ±0.05 ±0.06 ±0.07 ±0.08 ±0.09 ±0.11 ±0.13 ±0.15 ±0.17 ±0.19 | - ±0.07 ±0.08 ±0.09 ±0.10 ±0.11 ±0.13 ±0.15 ±0.17 ±0.19 |