牌号 | 化学成分(质量分数)/% | ||||||||||||||
Cb | Si | Mn | Cr | Ni | Mo | Nb | V | P | S | Alt | Cu | Ti | B | Ca | |
Q245Ra | ≤0.20 | ≤0.35 | 0.50~1.00c | ≤涂覆0.025 | ≤0.010 | ≥0.020 | |||||||||
Q345Ra | ≤0.20 | ≤0.55 | 1.20~1.60 | ≤0.025 | ≤0.010 | ≥0.020 | |||||||||
Q370R | ≤0.18 | ≤0.55 | 1.20~1.60 | 0.015~0.050 | ≤0.020 | ≤0.010 | |||||||||
17MnNiVNbR | ≤0.20 | 0.20~0.55 | 1.30~1.70 | 0.20~0.50 | 0.010~ 0.040 | 0.02~0.08 | ≤0.020 | ≤0.010 | |||||||
18MnMoNbR | ≤0.22 | 0.15~0.50 | 1.20~1.60 | 0.45~0.65 | 0.025~0.050 | ≤0.020 | ≤0.010 | ||||||||
13MnNiMoR | ≤0.15 | 0.15~0.50 | 1.20~1.60 | 0.20~0.40 | 0.60~1.00 | 0.20~0.40 | 0.005~0.020 | ≤0.020 | ≤0.010 | ||||||
15CrMoR | 0.12~0.18 | 0.15~0.40 | 0.40~0.70 | 0.80~1.20 | 0.45~0.60 | ≤0.025 | ≤0.010 | ||||||||
14Cr1MoR | 0.05~0.17 | 0.50~0.80 | 0.40~0.65 | 1.15~1.50 | 0.45~0.65 | ≤0.020 | ≤0.010 | ||||||||
12Cr2Mo1R | 0.08~0.15 | ≤0.50 | 0.30~0.60 | 2.00~2.50 | 0.90~1.10 | ≤0.020 | ≤0.010 | ||||||||
12Cr1MoVR | 0.08~0.15 | 0.15~0.40 | 0.40~0.70 | 0.90~1.20 | 0.25~0.35 | 0.15~0.30 | ≤0.025 | ≤0.010 | |||||||
12Cr2Mo1VR | 0.11~0.15 | ≤0.10 | 0.30~0.60 | 2.00~2.50 | ≤0.25 | 0.90~1.10 | ≤0.07 | 0.25~0.35 | ≤0.010 | ≤0.005 | ≤ 0.20 | ≤ 0.030 | ≤ 0.0020 | ≤ 0.015 | |
a 如果钢中加入Nb、Ti、V等微量元素,Alt含量的下限不适用。 b经供需双方协议,并在合同中注明,C含量下限可不作要求。 c厚度大于60mm的钢板,Mn含量上限可至1.20%。 | |||||||||||||||
牌号 | 交货状态 | 钢板厚度 mm | 拉伸试验 | 冲击试验 | 弯曲试验 | |||
抗拉强度Rm,N/mm2 | 屈服强度a ReL,N/mm2 | 伸长率A,% | 温度 ℃ | 冲击吸收能量 KV2,J | 180° b=2a | |||
不小于 | 不小于 | |||||||
Q245R | 热轧 控轧 或 正火 | 3~16 | 400~520 | 245 | 25 | 0 | 34 | d=1.5a |
>16水平多关节机器人~36 | 235 | |||||||
36~60 | 225 | |||||||
60~100 | 390~510 | 205 | 24 | d=2a | ||||
100~150 | 380~500 | 185 | ||||||
Q345R | 3~16 | 510~实心锥形喷嘴640 | 345 | 21 | 0 | 41 | d=2a | |
>16~36 | 500~630 | 325 | d=3a | |||||
>36~60 | 490~620 | 315 | ||||||
>60~100 | 490~620 | 305 | 20 | |||||
>100~150 | 480~610 | 285 | ||||||
>150~200 | 470~600 | 265 | ||||||
Q370R | 正火 | 10~16 | 530~630 | 370 | 20 | -20 | 47 | d=2a |
>16~36 | 360 | d=3a | ||||||
>36~60 | 520~620 | 340 | ||||||
>60~100 | 510~610 | 330 | ||||||
17MnNiVNbR | 正火 | 10~20 | 590~720 | 410 弧齿 | 20 | -20 | 60燃气吹灰器 | d=3a |
>20~30 | 570~700 | 390 | ||||||
18MnMoNbR | 正火 加 回火 | 30~60 | 570~720 | 400 | 17 | 0 | 47 | d=3a |
>60~100 | 390 | |||||||
13MnNiMoR | 30~100 | 570~720 | 390 | 18 | 0 | 47 | d=3a | |
>100~150 | 380 | |||||||
15CrMoR | 正火 加 回火 | 6~60 | 450~590 | 295 | 19 | 20 | 47 | d=3a |
>60~100 | 275 | |||||||
>100~200 | 440~580 | 255 | ||||||
14Cr1MoR | 6~100 | 520~680 | 310 | 19 | 20 | 47 | d=3a | |
>100~200 | 510~670 | 300 | ||||||
12Cr2Mo1R | 6~200 | 520~680 | 310 | 19 | 20 | 47 | d=3a | |
12Cr1MoVR | 6~60 | 440~590 | 245 | 19 | 20 | 47 | d=3a | |
>60~100 | 430~580 | 235 | ||||||
12Cr2Mo1VR | 6~200 | 590~760 | 415 | 17 | -20 | 60 | d=3a | |
a如屈服现象不明显,屈服强度取Rp0.2。 | ||||||||