橡胶专业词汇

橡胶专业英文词汇

橡胶工艺学－Principles of Rubber

Processing

橡胶－Rubber

聚合物－Polymer

拉伸强度－Tensile strength

定伸应力－Modulus

撕裂强度－Tear Strength

拉断伸长率－Elongation at break

永久变形－Permanent Set

回弹性－Resilience

硬度－Hardness

磨耗－Abrasion Resistance

抗湿滑性－Wet Skid Resistance

生热－Heat build-up

门尼粘度－Mooney Viscosity

生胶－Gum

混炼胶－Compound

硫化胶－Vulcanizate

硫化体系－Curing System

补强填充体系－Reinforcing agents and Filler

防护体系－antiagent

增塑体系－Plasticizer

塑炼－Plasticate

混炼－Mixing or compounding

压延－Calendering

压出－Extruding

硫化－Curing or Crosslinking or Vulcanizing

韩泰－Hancock

固特异－Goodyear

邓录普－Dunlop

生胶－Raw Rubber

天然橡胶－NR

丁苯橡胶－SBR

顺丁橡胶－BR

橡胶－NBR

氯丁橡胶－CR

乙丙橡胶－EPM,EPDM

丁基橡胶－IIR

异戊橡胶－IR

氟橡胶－FPM

硅橡胶－MVQ or Q

聚氨酯橡胶－PU

丙烯酸酯橡胶－ACM

聚硫橡胶－T

氯化聚乙烯－CPE

氯磺化聚乙烯－CSM

聚醚橡胶或氯醇橡胶－CO,ECO

环氧化天然橡胶－ENR

配合与加工－Compound and Processing

粉末橡胶－Powder Rubber

胶粉－Crumb，ground rubber

再生胶－Reclaimed rubber

硫化体系－Curing System

硫化仪－valcameter

高铁－Gotech

硫化曲线－Curing curve

诱导期－Induction time

焦烧时间－Scorch time

焦烧－Scorch

工艺正硫化时间（T90）－Optimum curing

time

理论正硫化时间－Theoretical curing time

硫化返原－Curing reversion

喷霜－Bloom

促进剂－Accelerating agent or Accelerator

活性剂－Activating agent or Activator

噻唑类－Thiazoles

次磺酰胺类－Sulfenamides

秋兰姆类－Thiuramsulfides

二硫代氨基甲酸盐类－Dithiocarbamates

胍类－Guanidines

硫脲类－Thioureas

醛胺类－Aldehyde amines

磺酸盐类－Xanthate

普通硫磺硫化体系－Conventional

Vulcanization CV

有效硫化体系－Effective Vulcanization EV

半有效硫化体系－Semi Effective

Vulcanization SEV

平衡硫化体系－Equilibrium cure EC

过氧化物硫化体系－Peroxide curing

systems

金属氧化物硫化体系－Metallic oxides 炭黑粒径－Particle size of CB

树脂硫化体系－Resin curing system 炭黑比表面积－Specific surface area of CB

补强与填充体系－Reinforcing and filling 解缠结——disentanglement

system

缺陷——imperfection，defect

补强－Reinforcing 模拟、模仿——simulation

填充－Filling 环氧树脂——epoxy炭黑－Carbon Black

氮气吸附－Nitrogen absorption

碘吸附－Iodine absorption

结构－Structure

微观结构－Microstructure

炭黑粒子－Carbon Black Particle

聚集体－Aggregate

附聚体－Agglomerate

颗粒－Pellet

表面性质－surface activity

凝胶－bonded rubber

化学吸附－Chemical absorption

物理吸附－Physical absorption

包容胶－Occluded rubber

应力软化效应－Stress softening effect

气相法白炭黑－Cas phase silica

沉淀法白炭黑－Precipitated silica

有机补强剂－organic reinforcer

偶联剂－Coupling agent

表面活性剂－Surfactant

老化－Aging

防护－Stabilization

塑炼－Mastication or Plastication

开炼机－Open roll mill or Open mixer or Rolling mill

密炼机－Internal mixer

混炼工艺－Compounding process

压延工艺－Calendering process

挤出工艺－Extrusion process

耐候性—weather resistance

橡胶片—rubber laminates

Panye效应是在小振幅循环载荷条件下产生的，表示的是橡胶粘弹储能模量对所施加应力振幅的依赖性。在应力振幅在大约0.1% 以上时，储能模量会随着振幅的增加而迅速下降；在应力振幅足够大（大概20%）时，储能模量达到一个下限值；在储存模量降低的区域，损耗模量出现最大值。 这一效应取决于材料中的填料含量，对于未填充弹性体则不起作用。从物理变化的角度，Payne效应可以归因于材料微观结构的变形诱导变化，也就是说填料团簇附近弱物理键的破坏和修复过程。由于Payne效应从本质上是橡胶弹性元件、汽车轮胎及其他产品中由频率和振幅所决定的动态稳定和阻尼行为，过去已经发展出了一些构建模型来构建这一效应 （比如Lion等人2003年的成果）。 与小形变下的Payne效应类似，大形变下所观察到的现象称为Mulins效应。